4 Layer Rogers Mixed FR4 Wifi Antenna pcb boards With 5.8 GHz 3 Oz Copper Through Hole Via
Products Details
| Raw Material | Rogers |
| Layer Count | Multilayer |
| Board Thickness | 0.8mm |
| Copper Thickness | 3.0oz |
| Surface Finish | Tin |
| Solder Mask | Black |
| Silkscreen | White |
| Min. Trace Width/Spacing | 0.075/0.075mm |
| Min. Hole Size | 0.25mm |
| Hole Wall Copper Thickness | ≥20μm |
| Measurement | 480×480mm |
| Packaging | Inner: Vacuum-packed in soft plastic bales
Outer: Cardboard Cartons with double straps |
| Application | Communication,automobile,cell,computer,medical |
| Advantage | Competitive Price,Fast Delivery,OEM&ODM,Free Samples, |
| Special Requirements | Buried And Blind Via, Impedance Control, Via Plug,
BGA Soldering And Gold Finger Are Acceptable |
| Certification | UL,ISO9001:2008,ROHS,REACH,SGS,HALOGEN-FREE |
Parameter:
Rogers 4003 C Pcb With 3.38 ER . There are 0.127 mm ,0.254 mm ,0.762 mm 0.508 mm 1.6 mm board thinckness with 1 oz , 2 oz ,3 oz .
Rogers 4350 B pcb With 3.5 ER . There are 0.127 mm ,0.254 mm ,0.762 mm 0.508 mm 1.6 mm board thinckness with 1 oz , 2 oz ,3 oz .
Rogers 5880 Pcb With 2.2 ER . There are 0.127 mm ,0.254 mm ,0.762 mm 0.508 mm 1.6 mm board thinckness with 1 oz , 2 oz ,3 oz .
PrePreg Material
| Parameter | Value |
| Specific gravity/density | 1.850 g/cm3 (3,118 lb/cu yd) |
| Water absorption | −0.125 in < 0.10% |
| Temperature index | 140 °C (284 °F) |
| Thermal conductivity, through-plane | 0.29 W/(m·K), 0.343 W/(m·K) |
| Thermal conductivity, in-plane | 0.81 W/(m·K), 1.059 W/(m·K) |
| Rockwell hardness | 110 M scale |
| Bond strength | > 1,000 kg (2,200 lb) |
| Flexural strength (A; 0.125 in) - LW | > 440 MPa (64,000 psi) |
| Flexural strength (A; 0.125 in) - CW | > 345 MPa (50,000 psi) |
| Tensile strength (0.125 in) LW | > 310 MPa (45,000 psi) |
| Izod impact strength - LW | > 54 J/m (10 ft·lb/in) |
| Izod impact strength - CW | > 44 J/m (8 ft·lb/in) |
| Compressive strength - flatwise | > 415 MPa (60,200 psi) |
| Dielectric breakdown (A) | > 50 kV |
| Dielectric breakdown (D48/50) | > 50 kV |
| Dielectric strength | 20 MV/m |
| Relative permittivity (A) | 4.8 |
| Relative permittivity (D24/23) | 4.8 |
| Dissipation factor (A) | 0.017 |
| Dissipation factor (D24/23) | 0.018 |
| Dielectric constant permittivity | 4.70 max., 4.35 @ 500 MHz, 4.34 @ 1 GHz |
| Glass transition temperature | Can vary, but is over 120 °C |
| Young's modulus - LW | 3.5×106 psi (24 GPa) |
| Young's modulus - CW | 3.0×106 psi (21 GPa) |
| Coefficient of thermal expansion - x-axis | 1.4×10−5 K−1 |
| Coefficient of thermal expansion - y-axis | 1.2×10−5 K−1 |
| Coefficient of thermal expansion - z-axis | 7.0×10−5 K−1 |
| Poisson's ratio - LW | 0.136 |
| Poisson's ratio - CW | 0.118 |
| LW sound speed | 3602 m/s |
| SW sound speed | 3369 m/s |
| LW Acoustic impedance | 6.64 MRayl |
Competitive Advantage:
1) With UL,ROHS,ISO,IPC
2).Lead time:3-10 working days
3)Competitive price best quality
4).Rich 20 years experience in High Tg Multilayer PCB .
What Information customer need to provide for quotation ?
1. PCB Gerber files ,protel,powerpcb,Autocad,etc.
2. BOM list for PCB assembly.
3. Send us your sample PCB or PCBA.
4. OEM is acceptable.
Product Tags:
|
|
4 Layer Rogers Mixed FR4 Wifi Antenna pcb boards With 5.8 GHz 3 Oz Copper Through Hole Via Images
|